Polyfenylenoxid mod. s 30 % skleněných vláken (PPO GF30)



We use this material in the following process(es):

Extrusion.
Extruded profiles and semifinished products

Machined parts.
Lathed and milled parts in single and serial production

Injection moulding.
Injection moulded parts up to 16.000 g

Thermoplastic structure foaming (TSF).
Multi functional parts and housings up to 16 kg


Material number   2233  
Density ISO 1183 1,3 g/cm3
   

Mechanical properties

Tensile strength ISO 527 100 MPa
Elongation at break ISO 527 1,5 %
Tensile modulus ISO 527 8000 MPa
Ball pressure hardness ISO 2039-1 130 MPa
Standard for ball pressure hardness   H358/30  
Hardness Shore (A/D) or Rockwell (R/L/M) ISO 868, ISO 2039-2 M93 -
   

Electrical properties

Dielectric constant at 50 Hz IEC 60250 2,9 -
Dielectric constant at 1 MHz IEC 60250 2,9 -
Dissipation factor at 50 Hz IEC 60250 6 1E-4
Dissipation factor at 1 MHz IEC 60250 10 1E-4
Dielectric strength IEC 60243-1 18 3) kV/mm
Thickness for electric strength   3,2 mm
Volume resistivity IEC 60093 1,00E+15 Ohm · m
Surface resistivity IEC 60093 1,00E+13 Ohm
Comparative tracking index IEC 60112 250 -
   

Thermal properties

Thermal conductance DIN 52 612 0,28 W/K m
Linear thermal expansion along|cross to direction of flow ISO 11359 30|70 10-6/K
Melting point or glass transition temp. ISO 11357 155 24) °C
Heat distortion temperature A ISO 75 HDT/A (1.8 MPa) 140 °C
Heat distortion temperature B ISO 75 HDT/B (0,45 MPa) 145 °C
Short time use temperature   130 °C
Continuous use temperature   110 °C
Minimal use temperature   -50 °C
   

Other properties

Humidity absorption at 23°C/50% ISO 62 0,06 %
Water absorption ISO 62 0,2 %
Flammability UL 94 IEC 60695-11-10 HB -
Thickness for UL 94   1,5 mm
Transparency (opaque/translucent/clear)   opaque  
Raw material   Noryl GFN3 (Sabic)  
   

3) : measured according to ASTM

24) : Softening point according to Vicat VST/A/120

This datasheet is a print-out of the material database RIWETA 4.0 and is intended for personal use only.

The figures in this datasheet are guide values. The values are affected by processing conditions, modifications, additives and environmental conditions and they do not release you from the obligation to check the validity and to undertake tests on your own. The information given is based on our state of knowledge. The material data is not to be construed as guaranteeing specific properties and the data can not be used to deduce the suitability for a particular application.

It remains the responsibility of the user of our products not to infringe patent rights and to comply with existing laws and regulations.